DX10311 is 30% glass fiber reinforced, impact modified polycarbonate resin. High flow and good ductility
| Original Document | Technical Datasheet(English) | |||
| Features | High ImpactGood ToughnessHigh FlowFilled & Reinforced | |||
| Additive | Impact Modifier | |||
| Reinforced | 30% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Melt Volume Flow Rate(MVR) | |||
300°C/5.0 kg | *** cm³/10 min | ISO 1133 | |
Mold Shrinkage | |||
Flow | ***~*** % | Internal | flow, 3.2 mm |
Across Flow | ***~*** % | Internal | xflow, 3.2 mm |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ASTM D638 | 5 mm/min |
Tensile Modulus | *** Mpa | ISO 527 | 1 mm/min |
Tensile Strength | |||
Break | *** Mpa | ISO 527 | 5 mm/min |
Break | *** Mpa | ASTM D638 | Type I, 5 mm/min |
Tensile Elongation | |||
Break | *** % | ASTM D638 | Type I, 5 mm/min |
Break | *** % | ISO 527 | 5 mm/min |
Flexural Modulus | *** Mpa | ASTM D790 | |
Flexural Modulus | *** Mpa | ISO 178 | 2 mm/min |
Flexural Strength | |||
Yield | *** Mpa | ISO 178 | 2 mm/min |
Break | *** Mpa | ISO 178 | 2 mm/min |
- | *** Mpa | ASTM D790 | |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/2C | |
Charpy Unnotched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/2C | |
Izod Notched Impact Strengh | |||
23℃ (73℉) | *** J/m | ASTM D256 | |
Izod Unnotched Impact Strengh | |||
23℃ (73℉) | *** J/m | ASTM D4812 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ASTM D648 | 3.2 mm, unannealed |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6/°C | ASTM E831 | -40°C to 40°C, flow |
Across Flow | *** E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.