LNP THERMOCOMP D351 (experimental grade name as EXTC8143) is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: High modulus, good flatness, good ductility, Non-Brominated & Non-Chlorinated Flame Retardant.
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高韧性阻燃无氯无溴填充增强 | |||
| 添加助剂 | 阻燃剂 | |||
| 增强填充 | 玻纤 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.425 g/cm³ | ASTM D792 | |
熔体体积流动速率(MVR) | |||
300°C/2.16 kg | 20 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
300℃/2.16 kg | 25.2 g/10min | ASTM D1238 | |
收缩率 | |||
纵向(Flow) | 0.1~0.3 % | ASTM D 955 | flow, 24 hrs |
横向(Across Flow) | 0.1~0.3 % | ASTM D 955 | xflow, 24 hr |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 125 Mpa | ISO 527 | 5 mm/min |
断裂(brk) | 120 Mpa | ASTM D638 | Type I, 5 mm/min |
拉伸延伸率 | |||
断裂(brk) | 2.4 % | ASTM D638 | Type I, 5 mm/min |
弯曲强度 | |||
屈服(yld) | 169 Mpa | ISO 178 | 2 mm/min |
断裂(brk) | 179 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 8390 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 7520 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 9040 Mpa | ASTM D638 | 5 mm/min |
拉伸模量 | 9080 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 15 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | 39 kJ/m² | ISO 179/1eU | Edgew 80*10*4 sp=62mm |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 150 J/m | ASTM D256 | |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 508 J/m | ASTM D4812 | |
仪器化落镖冲击能量 | |||
23℃ (73℉)峰值 | 24 J | ASTM D3763 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 116 °C | ASTM D648 | 3.2 mm, unannealed |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 20.2 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
横向(Across Flow) | 67.4 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-0 | 0.8 mm | UL94 |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。