LNP STAT-KON UC1200 is a 12% carbon fiber reinforced PEI. High modulus with ESD characteristics for high-heat applications.
| Original Document | Technical Datasheet(English) | |||
| Features | Heat ResistanceElectrically ConductiveEMI/RFI ESDFilled & Reinforced | |||
| Reinforced | 12% Carbon Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Melt Mass Flow Rate(MFR) | |||
337°C/6.6 kg | *** g/10 min | ASTM D 1238 | |
Mold Shrinkage | |||
Flow | ***~*** % | Internal | flow, 3.2 mm |
Across Flow | ***~*** % | Internal | xflow, 3.2 mm |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ASTM D638 | 5 mm/min |
Tensile Strength | |||
Yield | *** Mpa | ASTM D638 | Type I, 5 mm/min |
Break | *** Mpa | ASTM D638 | Type I, 5 mm/min |
Tensile Elongation | |||
Yield | *** % | ASTM D638 | Type I, 5 mm/min |
Break | *** % | ASTM D638 | Type I, 5 mm/min |
Flexural Modulus | *** Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
Flexural Modulus | *** Mpa | ASTM D790 | 2.6 mm/min, 100 mm span |
Flexural Strength | |||
Break | *** Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
Break | *** Mpa | ASTM D790 | 2.6 mm/min, 100 mm span |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Izod Notched Impact Strengh | |||
23℃ (73℉) | *** J/m | ASTM D256 | |
Izod Unnotched Impact Strengh | |||
23℃ (73℉) | *** J/m | ASTM D4812 | |
Instrumented Impact Energy | |||
23℃ (73℉)Total Energy | *** J | ASTM D3763 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ASTM D648 | 3.2mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ASTM D648 | 3.2mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ASTM D648 | 6.4 mm, unannealed |
Vicat Softening Temperature(VST) | *** °C | ASTM D1525 | Rate B/50 |
Relative Temperature Index(RTI), Imp | |||
- | *** °C | UL 746B | |
Relative Temperature Index(RTI), Elec | |||
- | *** °C | UL 746B | |
Relative Temperature Index(RTI), Str | |||
- | *** °C | UL 746B | |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6/°C | ASTM E831 | -20°C to 150°C, flow |
Flow | *** E-6/°C | ASTM E831 | -40°C to 40°C, flow |
Across Flow | *** E-6/°C | ASTM E831 | -20°C to 150°C, xflow |
Across Flow | *** E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
V-0 | *** mm | UL94 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-cm | ASTM D257 | |
Surface Resistivity | *** Ohm | ASTM D257 | |
Hot Wire Ignition(HWI) | *** PLC | UL 746A | |
High Ampere Arc Ignition(HAI) | *** PLC | UL 746A | |
Static Decay | *** seconds | FTMS101B | 5000V to <50V |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.