LNP STAT-KON PX08019 is a compound based on PA 6 resin containing Glass Fiber, Carbon Fiber, Flame Retardant. Added features include; Non-Halogen Flame Retardant, Electrically Conductive.
| Original Document | Technical Datasheet(English) | |||
| Features | Flame RetardantHalogen FreeElectrically ConductiveFilled & Reinforced | |||
| Additive | Flame Retardant | |||
| Reinforced | Glass FiberCarbon FiberGlass Fiber+Carbon Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Mold Shrinkage | |||
Flow | ***~*** % | Internal | flow |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | |||
Yield | *** Mpa | ISO 527 | 5 mm/min |
Tensile Elongation | |||
Break | *** % | ISO 527 | 5 mm/min |
Flexural Modulus | *** Mpa | ISO 178 | 2 mm/min |
Flexural Strength | |||
Yield | *** Mpa | ISO 178 | 2 mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Izod Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 180/1A | 80*10*4 |
Izod Unnotched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 180/1U | 80*10*4 |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
V-0 | *** mm | UL94 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Surface Resistivity | ***~*** Ohm | ASTM D257 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.