LNP LUBRICOMP WAL34 is a compound based on (PBT resin containing 15% PTFE, 20% Aramid Fiber. Added features of this material include: Wear Resistant.
| Original Document | Technical Datasheet(English) | |||
| Features | Wear/Abrasion ResistanceFilled & Reinforced | |||
| Reinforced | 20% Aramid Fiber15% PTFE | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Mold Shrinkage | |||
Flow | *** % | ASTM D955 | flow, 24 hrs |
Across Flow | *** % | ASTM D955 | xflow, 24 hr |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ASTM D638 | 50 mm/min |
Tensile Strength | |||
Break | *** Mpa | ASTM D638 | |
Tensile Elongation | |||
Break | *** % | ASTM D638 | |
Flexural Modulus | *** Mpa | ASTM D790 | |
Flexural Strength | |||
- | *** Mpa | ASTM D790 | |
Coefficient of Friction | *** - | ASTM D 3702 | Dynamic COF |
Coefficient of Friction | *** - | ASTM D 3702 | Static COF |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ASTM D648 | 3.2 mm, unannealed |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.