LNP LUBRICOMP RFL36 is a compound based on Nylon 66 resin containing Glass Fiber, PTFE. Wear Resistant
| Original Document | Technical Datasheet(English) | |||
| Features | Wear/Abrasion ResistanceFilled & Reinforced | |||
| Reinforced | Glass FiberPTFEGlass Fiber+PTFE | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Volume Flow Rate(MVR) | |||
275°C/5 kg | ***~*** cm³/10 min | ISO 1133 | |
Mold Shrinkage | |||
Flow | *** % | ISO 294 | flow, 24 hrs |
Across Flow | *** % | ISO 294 | xflow, 24 hr |
Water Absorption | *** % | ISO 62-1 | 23°C/24hrs |
Moisture /Humidity Absorption | *** % | ISO 62 | 23°C / 50% RH |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | |||
Break | *** Mpa | ISO 527 | 5 mm/min |
Tensile Elongation | |||
Break | *** % | ISO 527 | 5 mm/min |
Flexural Modulus | *** Mpa | ISO 178 | 2 mm/min |
Flexural Modulus | *** Mpa | ISO 178 | 2 mm/min, 100°C |
Flexural Modulus | *** Mpa | ISO 178 | 2 mm/min, 150°C |
Flexural Modulus | *** Mpa | ISO 178 | 2 mm/min, 200°C |
Flexural Modulus | *** Mpa | ISO 178 | 2 mm/min, 60°C |
Flexural Strength | |||
Yield | *** Mpa | ISO 178 | 2 mm/min |
Yield | *** Mpa | ISO 178 | 2 mm/min, 100°C |
Yield | *** Mpa | ISO 178 | 2 mm/min, 150°C |
Yield | *** Mpa | ISO 178 | 2 mm/min, 200°C |
Yield | *** Mpa | ISO 178 | 2 mm/min, 60°C |
Break | *** Mpa | ISO 178 | 2 mm/min |
Flexural Strain | |||
break | *** % | ISO 178 | 2 mm/min |
break | *** % | ISO 178 | 2 mm/min, 100°C |
break | *** % | ISO 178 | 2 mm/min, 150°C |
break | *** % | ISO 178 | 2 mm/min, 200°C |
break | *** % | ISO 178 | 2 mm/min, 60°C |
Coefficient of Friction | *** - | ASTM D 3702 | Dynamic COF |
Wear Factor | *** E-10 in5·min/ft·lb·hr | ASTM D 3702 | Wear Factor Washer |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Izod Notched Impact Strengh | |||
-40℃ (-40℉) | *** kJ/m² | ISO 180/1A | 80*10*3 |
23℃ (73℉) | *** kJ/m² | ISO 180/1A | 80*10*4 |
Izod Unnotched Impact Strengh | |||
-40℃ (-40℉) | *** kJ/m² | ISO 180/1U | 80*10*4 |
23℃ (73℉) | *** kJ/m² | ISO 180/1U | 80*10*4 |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
Specific Heat | *** J/kg-K | ASTM E 1269 | |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6/°C | ISO 11359-2 | 23°C to 60°C, flow |
Across Flow | *** E-6/°C | ISO 11359-2 | 23°C to 60°C, xflow |
Thermal Conductivity | *** W/(m K) | ASTM D 5930 | |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
HB | *** mm | UL94 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.