LNP LUBRICOMP KG002 is a compound based on Acetal Copolymer resin containing 10% Graphite. Added feature of this material is: Wear Resistant.
| Original Document | Technical Datasheet(English) | |||
| Features | Wear/Abrasion ResistanceCopolymer | |||
| Reinforced | 10% Graphite | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Mold Shrinkage | |||
Flow | *** % | ISO 294 | flow, 24 hrs |
Flow | *** % | ASTM D955 | flow, 24 hrs |
Across Flow | *** % | ASTM D955 | xflow, 24 hr |
Across Flow | *** % | ISO 294 | xflow, 24 hr |
Moisture /Humidity Absorption | *** % | ASTM D 570 | 50% RH, 24 hrs |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ASTM D638 | 50 mm/min |
Tensile Modulus | *** Mpa | ISO 527 | 1 mm/min |
Tensile Strength | |||
Yield | *** Mpa | ASTM D638 | |
Yield | *** Mpa | ISO 527 | |
Break | *** Mpa | ISO 527 | |
Break | *** Mpa | ASTM D638 | |
Tensile Elongation | |||
Yield | *** % | ASTM D638 | |
Yield | *** % | ISO 527 | |
Break | *** % | ASTM D638 | |
Break | *** % | ISO 527 | |
Flexural Modulus | *** Mpa | ASTM D790 | |
Flexural Modulus | *** Mpa | ISO 178 | |
Flexural Strength | |||
- | *** Mpa | ISO 178 | |
Coefficient of Friction | *** - | ASTM D 3702 | Dynamic COF |
Coefficient of Friction | *** - | ASTM D 3702 | Static COF |
Wear Factor | *** E-10 in5·min/ft·lb·hr | ASTM D 3702 | Wear Factor Washer |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Izod Notched Impact Strengh | |||
23℃ (73℉) | *** J/m | ASTM D256 | |
23℃ (73℉) | *** kJ/m² | ISO 180/1A | 80*10*4 |
Izod Unnotched Impact Strengh | |||
23℃ (73℉) | *** J/m | ASTM D4812 | |
23℃ (73℉) | *** kJ/m² | ISO 180/1U | 80*10*4 |
Instrumented Impact Energy | |||
23℃ (73℉)peak | *** J | ASTM D3763 | |
Multiaxial Impact | *** J | ISO 6603 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ASTM D648 | 3.2 mm, unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6/°C | ASTM E831 | -40°C to 40°C, flow |
Flow | *** E-6/°C | ISO 11359-2 | -40°C to 40°C, flow |
Across Flow | *** E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
Across Flow | *** E-6/°C | ISO 11359-2 | -40°C to 40°C, xflow |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.