35% Glass Fiber Reinforced, Laser Direct Structuring (LDS), Low Warpage
ForTii® Eco LDS62B is a high ductility LDS material which enables good structural integrity in complicated geometries. It is well suited for wearable devices and smart phone antennas for consumer electronics. It has excellent dimensional stability to ensure low warpage after chemical plating. Eco LDS62B is Eco-friendly due to its partly bio-based content.
| 原厂资料 | 物性表(英文) | |||
| 树脂缩写 | PA-GF35 | |||
| 产品特性 | 尺寸稳定低翘曲电镀激光直接成型(LDS)生物基填充增强 | |||
| 应用产品 | 智能手机天线可穿戴设备 | |||
| 应用行业 | 电子电器 | |||
| 成型方式 | 注塑 | |||
| 生物基可再生 | 是 | |||
| 增强填充 | 35% 玻纤 | |||
| 物理性能 | 干态/湿态 | 单位 | 测试标准 | 测试条件 |
|---|---|---|---|---|
密度 | 1.5/ - | g/cm³ | ISO 1183 | |
收缩率 | ||||
纵向(Flow) | 0.21/ * | % | ISO 294-4 | |
横向(Across Flow) | 0.7/ * | % | ISO 294-4 | |
| 机械性能 | 干态/湿态 | 单位 | 测试标准 | 测试条件 |
拉伸强度 | ||||
断裂(brk) | 130/ - | Mpa | ISO 527-1/-2 | |
拉伸延伸率 | ||||
断裂(brk) | 1.7/ - | % | ISO 527-1/-2 | |
弯曲强度 | ||||
- | 190/ - | Mpa | ISO 178 | |
弯曲模量 | 10000/ - | Mpa | ISO 178 | |
拉伸模量 | 11500/ - | Mpa | ISO 527-1/-2 | |
| 冲击性能 | 干态/湿态 | 单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | ||||
23℃ (73℉) | 4.6/ - | kJ/m² | ISO 179/1eA | |
| 热学性能 | 干态/湿态 | 单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | ||||
1.8 Mpa (264 psi)（18.6kg/cm²） | 235/ * | °C | ISO 75-1/-2 | |
线性膨胀系数(CLTE) | ||||
纵向(Flow) | 17/ * | E-6/°C | ISO 11359-1/-2 | |
横向(Across Flow) | 66/ * | E-6/°C | ISO 11359-1/-2 | |
熔融温度(Tm) | 319/ * | °C | ISO 11357-1/-3 | |
| 燃烧性能 | 干态/湿态 | 单位 | 测试标准 | 测试条件 |
UL 防火等级 | ||||
HB | 1.5/ * | mm | UL94 | |
HB | 3/ * | mm | UL94 | |
HB | 1.5/ * | mm | IEC 60695-11-10 | |
HB | 3/ * | mm | IEC 60695-11-10 | |
| 电学性能 | 干态/湿态 | 单位 | 测试标准 | 测试条件 |
介电常数(DK) | ||||
1 GHz | 3.74/ 3.8 | - | IEC 61189-2-721 |