Heat stabilized, partially aromatic polyphthalamide for injection molding with strong mechanical properties especially at elevated temperatures and excellent chemical resistance for highly stressed parts. The product can be characterized as compound with high strength and stiffness, very low water absorption and outstanding dimensional stability. It features a high melting point (320°C) and excellent melt stability.
Markets & applications
Automotive: Fuel system, cooling system, powertrain, thermostat housing, pumps, fuel cell
E&E: Sensors, SMT applications (surface mount technology)
Industry goods: Pumps, compressors
Consumer goods: home appliances, consumer electronics, furniture fittings
原厂资料 | 物性表(英文) | |||
产品特性 | 耐热热稳定尺寸稳定耐化学性低吸湿性填充增强 | |||
添加助剂 | 热稳定剂 | |||
颜色形状 | 粒状黑色 | |||
成型方式 | 注塑 | |||
应用产品 | 家用电器配件汽车零部件工业用品节温器外壳表面贴装(SMT)高应力部件传感器 | |||
增强填充 | 35% 玻纤 |
物理性能 | 值/单位 | 测试标准 | 测试条件 |
---|---|---|---|
密度 | 1.485 g/cm³ | ISO 1183 | |
收缩率 | |||
纵向(Flow) | 0.4 % | ISO 294-4 | |
横向(Across Flow) | 0.93 % | ISO 294-4 | |
吸水率 | 0.41 % | ISO 62 | 24 h in water, 23 °C |
吸水率 | 3.8 % | ISO 62 | saturation in water at 23°C |
吸湿率 | 1.6 % | ISO 62 | equilibrium 23°C/50% r.h. |
粘度 | 105 cm³/g | ISO 307, 1157, 1628 | 0.5% in 96% H2SO4 |
机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 210 Mpa | ISO 527-1/-2 | Cond., 23°C |
断裂(brk) | 145 Mpa | ISO 527-1/-2 | Cond., 80°C |
断裂(brk) | 135 Mpa | ISO 527-1/-2 | Dry, 120°C |
断裂(brk) | 70 Mpa | ISO 527-1/-2 | Dry, 170°C |
断裂(brk) | 220 Mpa | ISO 527-1/-2 | Dry, 23°C |
断裂(brk) | 180 Mpa | ISO 527-1/-2 | Dry, 80°C |
拉伸延伸率 | |||
断裂(brk) | 1.9 % | ISO 527-1/-2 | Cond., 23°C |
断裂(brk) | 2.2 % | ISO 527-1/-2 | Cond., 80°C |
断裂(brk) | 2.9 % | ISO 527-1/-2 | Dry, 120°C |
断裂(brk) | 6.5 % | ISO 527-1/-2 | Dry, 170°C |
断裂(brk) | 2 % | ISO 527-1/-2 | Dry, 23°C |
断裂(brk) | 2 % | ISO 527-1/-2 | Dry, 80°C |
弯曲强度 | |||
- | 290 Mpa | ISO 178 | Cond. |
- | 300 Mpa | ISO 178 | Dry |
弯曲模量 | 13000 Mpa | ISO 178 | Cond., 23°C |
弯曲模量 | 13000 Mpa | ISO 178 | Dry, 23°C |
拉伸模量 | 14000 Mpa | ISO 527-1/-2 | Cond., 23°C |
拉伸模量 | 12000 Mpa | ISO 527-1/-2 | Cond., 80°C |
拉伸模量 | 10000 Mpa | ISO 527-1/-2 | Dry, 120°C |
拉伸模量 | 4400 Mpa | ISO 527-1/-2 | Dry, 170°C |
拉伸模量 | 14000 Mpa | ISO 527-1/-2 | Dry, 23°C |
拉伸模量 | 12500 Mpa | ISO 527-1/-2 | Dry, 80°C |
冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 8 kJ/m² | ISO 179/1eA | Dry |
23℃ (73℉) | 8 kJ/m² | ISO 179/1eA | Dry |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | 70 kJ/m² | ISO 179/1eU | Dry |
23℃ (73℉) | 70 kJ/m² | ISO 179/1eU | Dry |
热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)(18.6kg/cm²) | 280 °C | ISO 75-1/-2 | |
比热容 | 1.07 J/kg-K | - | 23°C |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 22 E-6/K | ISO 11359-1/-2 | (23-55)°C |
横向(Across Flow) | 51~53 E-6/K | ISO 11359-1/-2 | (23-55)°C |
熔融温度(Tm) | 320 °C | ISO 11357-1/-3 | DSC |
导热系数 | 0.344 W/(m K) | DIN 52612-1 | solid material (40°C) |
加工温度 | 335~355 °C | - | Injection moulding/Extrusion |
加工温度 | 350 °C | - | Test specimen production |
模具温度 | 140~170 °C | - | Injection moulding |
模具温度 | 150 °C | - | Test specimen production |
电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 4.3E+8 Ohm-m | IEC 60093 | Dry, 150°C |
体积电阻率 | 1.0E+15 Ohm-m | IEC 62631-3-1 | Cond. |
体积电阻率 | 1.0E+15 Ohm-m | IEC 62631-3-1 | Dry |
表面电阻率 | 1.0E+15 Ohm | IEC 62631-3-2 | Cond. |
相比漏电起痕指数(CTI ) | |||
溶液A | 600 V | IEC 60112 | |
绝缘强度 | 37 kV/mm | IEC 60243-1 | Dry, K20/K20, (60*60*1 mm³) |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。