Heat stabilized, partially aromatic polyphthalamide for injection molding with strong mechanical properties especially at elevated temperatures, and excellent chemical resistance for highly stressed parts. Ultramid® Advanced T1000HG10 LS BK can be characterized as compound with high strength and stiffness, very low water absorption and outstanding dimensional stability. It features a high melting point (320°C) and excellent melt stability.
Markets & applications
Automotive: Fuel system, cooling system, powertrain, metal replacement
Industry goods: Pumps, compressors
Consumer goods: Home appliances, consumer electronics, furniture fittings
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐热热稳定尺寸稳定耐化学性低吸湿性填充增强 | |||
| 颜色形状 | 粒状黑色 | |||
| 成型方式 | 注塑 | |||
| 应用产品 | 金属替代高应力部件 | |||
| 增强填充 | 50% 玻纤 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.642 g/cm³ | ISO 1183 | |
收缩率 | |||
纵向(Flow) | 0.5 % | ISO 294-4 | |
横向(Across Flow) | 0.87 % | ISO 294-4 | |
吸水率 | 0.27 % | ISO 62 | 24 h in water, 23 °C |
吸水率 | 2.9 % | ISO 62 | saturation in water at 23°C |
吸湿率 | 1.3 % | ISO 62 | equilibrium 23°C/50% r.h. |
粘度 | 100 cm³/g | ISO 307, 1157, 1628 | 0.5% in 96% H2SO4 |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 300 Mpa | ISO 527-1/-2 | Cond., -30°C |
断裂(brk) | 120 Mpa | ISO 527-1/-2 | Cond., 120°C |
断裂(brk) | 70 Mpa | ISO 527-1/-2 | Cond., 170°C |
断裂(brk) | 250 Mpa | ISO 527-1/-2 | Cond., 23°C |
断裂(brk) | 200 Mpa | ISO 527-1/-2 | Cond., 80°C |
断裂(brk) | 270 Mpa | ISO 527-1/-2 | Dry, -30°C |
断裂(brk) | 160 Mpa | ISO 527-1/-2 | Dry, 120°C |
断裂(brk) | 80 Mpa | ISO 527-1/-2 | Dry, 170°C |
断裂(brk) | 250 Mpa | ISO 527-1/-2 | Dry, 23°C |
断裂(brk) | 220 Mpa | ISO 527-1/-2 | Dry, 80°C |
拉伸延伸率 | |||
断裂(brk) | 2 % | ISO 527-1/-2 | Cond., -30°C |
断裂(brk) | 3.4 % | ISO 527-1/-2 | Cond., 120°C |
断裂(brk) | 5.3 % | ISO 527-1/-2 | Cond., 170°C |
断裂(brk) | 1.8 % | ISO 527-1/-2 | Cond., 23°C |
断裂(brk) | 2 % | ISO 527-1/-2 | Cond., 80°C |
断裂(brk) | 1.8 % | ISO 527-1/-2 | Dry, -30°C |
断裂(brk) | 2.6 % | ISO 527-1/-2 | Dry, 120°C |
断裂(brk) | 6 % | ISO 527-1/-2 | Dry, 170°C |
断裂(brk) | 1.8 % | ISO 527-1/-2 | Dry, 23°C |
断裂(brk) | 2.1 % | ISO 527-1/-2 | Dry, 80°C |
拉伸模量 | 18000 Mpa | ISO 527-1/-2 | Cond., -30°C |
拉伸模量 | 14000 Mpa | ISO 527-1/-2 | Cond., 120°C |
拉伸模量 | 5500 Mpa | ISO 527-1/-2 | Cond., 170°C |
拉伸模量 | 18000 Mpa | ISO 527-1/-2 | Cond., 23°C |
拉伸模量 | 17500 Mpa | ISO 527-1/-2 | Cond., 80°C |
拉伸模量 | 18000 Mpa | ISO 527-1/-2 | Dry, -30°C |
拉伸模量 | 15000 Mpa | ISO 527-1/-2 | Dry, 120°C |
拉伸模量 | 6000 Mpa | ISO 527-1/-2 | Dry, 170°C |
拉伸模量 | 18000 Mpa | ISO 527-1/-2 | Dry, 23°C |
拉伸模量 | 17500 Mpa | ISO 527-1/-2 | Dry, 80°C |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 10 kJ/m² | ISO 179/1eA | Cond. |
-30℃ (-22℉) | 10 kJ/m² | ISO 179/1eA | Dry |
23℃ (73℉) | 11 kJ/m² | ISO 179/1eA | Cond. |
23℃ (73℉) | 10 kJ/m² | ISO 179/1eA | Dry |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | 65 kJ/m² | ISO 179/1eU | Cond. |
-30℃ (-22℉) | 65 kJ/m² | ISO 179/1eU | Dry |
23℃ (73℉) | 70 kJ/m² | ISO 179/1eU | Cond. |
23℃ (73℉) | 75 kJ/m² | ISO 179/1eU | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 280 °C | ISO 75-1/-2 | |
比热容 | 0.646 J/kg-K | - | 23°C |
熔融温度(Tm) | 320 °C | ISO 11357-1/-3 | DSC |
导热系数 | 0.266 W/(m K) | DIN 52612-1 | solid material (40°C) |
加工温度 | 345~355 °C | - | Injection moulding/Extrusion |
加工温度 | 350 °C | - | Test specimen production |
模具温度 | 150~190 °C | - | Injection moulding |
模具温度 | 150 °C | - | Test specimen production |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+15 Ohm-m | IEC 62631-3-1 | Cond. |
体积电阻率 | 1.0E+16 Ohm-m | IEC 62631-3-1 | Dry |
表面电阻率 | 1.0E+15 Ohm | IEC 62631-3-2 | Cond. |
相比漏电起痕指数(CTI ) | |||
溶液A | 550 V | IEC 60112 | Cond., 23°C |
绝缘强度 | 40 kV/mm | IEC 60243-1 | Dry, K20/K20, (60*60*1 mm³) |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。