Partially aromatic, glassfiber reinforced polyphthalamide for injection molding with strong mechanical properties especially at elevated temperatures, good long-term thermal stability and outstanding chemical resistance for highly stressed parts. The product can be characterized as compound with high toughness, stiffness, extremely low water absorption and outstanding dimensional stability. It features high flowability and allows filling of complex parts with thin wall thickness. The product is easily processable with excellent melt stability.
Markets & applications
Automotive: Fuel system, cooling system, powertrain, Auto E&E, sensors, fuel cell
E&E: Connectors
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐热耐热老化尺寸稳定耐化学性高流动低吸湿性填充增强 | |||
| 颜色形状 | 粒状黑色 | |||
| 成型方式 | 注塑 | |||
| 应用产品 | 电子电器薄壁产品注塑汽车零部件连接器高应力部件 | |||
| 增强填充 | 30% 玻纤 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.37 g/cm³ | ISO 1183 | |
收缩率 | |||
纵向(Flow) | 0.5 % | ISO 294-4 | |
横向(Across Flow) | 1 % | ISO 294-4 | |
吸水率 | 0.2 % | ISO 62 | 24 h in water, 23 °C |
吸水率 | 2 % | ISO 62 | saturation in water at 23°C |
吸湿率 | 0.9 % | ISO 62 | equilibrium 23°C/50% r.h. |
粘度 | 100 cm³/g | ISO 307, 1157, 1628 | 0.5% in 96% H2SO4 |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 175 Mpa | ISO 527-1/-2 | Cond.,23°C |
断裂(brk) | 190 Mpa | ISO 527-1/-2 | Dry, 23°C |
拉伸延伸率 | |||
断裂(brk) | 2.2 % | ISO 527-1/-2 | Cond.,23°C |
断裂(brk) | 2.4 % | ISO 527-1/-2 | Dry, 23°C |
拉伸模量 | 10000 Mpa | ISO 527-1/-2 | Cond.,23°C |
拉伸模量 | 10000 Mpa | ISO 527-1/-2 | Dry, 23°C |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 7 kJ/m² | ISO 179/1eA | Cond. |
-30℃ (-22℉) | 8 kJ/m² | ISO 179/1eA | Dry |
23℃ (73℉) | 7 kJ/m² | ISO 179/1eA | Cond. |
23℃ (73℉) | 8 kJ/m² | ISO 179/1eA | Dry |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | 50 kJ/m² | ISO 179/1eU | Cond. |
-30℃ (-22℉) | 60 kJ/m² | ISO 179/1eU | Dry |
23℃ (73℉) | 50 kJ/m² | ISO 179/1eU | Cond. |
23℃ (73℉) | 60 kJ/m² | ISO 179/1eU | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 270 °C | ISO 75-1/-2 | |
熔融温度(Tm) | 300 °C | ISO 11357-1/-3 | DSC |
加工温度 | 320~340 °C | - | Injection moulding/Extrusion |
加工温度 | 330 °C | - | Test specimen production |
模具温度 | 125~170 °C | - | Injection moulding |
模具温度 | 140 °C | - | Test specimen production |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 0.8 mm | IEC 60695-11-10 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+14 Ohm-m | IEC 62631-3-1 | Cond. |
体积电阻率 | 1.0E+14 Ohm-m | IEC 62631-3-1 | Dry |
表面电阻率 | 1.0E+15 Ohm | IEC 62631-3-2 | Cond. |
相比漏电起痕指数(CTI ) | |||
溶液A | 600 V | IEC 60112 | Cond. |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。