Polyphthalamide, light colorable, with a high melting point, halogen-free flame-retardant, very low water absorption, good mechanical and dielectrical properties at elevated temperatures as well as excellent chemical resistance, soldering bath resistant. Colors available (e.g. Orange RAL 2003).
Markets & applications
Automotive: Automotive electrics & electronics (E&E), sensors, fuel cell, e-mobility
E&E: Connectors, SMT (surface mount technology) applications, energy distribution
Consumer goods: Home appliances, consumer electronics, cell phone parts
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 阻燃无卤耐化学性低吸湿性填充增强 | |||
| 添加助剂 | 阻燃剂 | |||
| 颜色形状 | 粒状可定制色橙色 | |||
| 成型方式 | 注塑 | |||
| 应用产品 | 电子电器家用电器配件汽车零部件表面贴装(SMT) | |||
| 增强填充 | 30% 玻纤 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.44 g/cm³ | ISO 1183 | |
熔体体积流动速率(MVR) | |||
325°C/5.0 kg | 30 cm³/10 min | ISO 1133 | |
收缩率 | |||
纵向(Flow) | 0.3 % | ISO 294-4 | |
横向(Across Flow) | 1 % | ISO 294-4 | |
吸水率 | 1.9~2.3 % | ISO 62 | saturation in water at 23°C |
吸湿率 | 0.7~1 % | ISO 62 | equilibrium 23°C/50% r.h. |
粘度 | 100 cm³/g | ISO 307, 1157, 1628 | 0.5% in 96% H2SO4 |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 130 Mpa | ISO 527-1/-2 | Cond., 23°C |
断裂(brk) | 140 Mpa | ISO 527-1/-2 | Dry, 23°C |
拉伸延伸率 | |||
断裂(brk) | 2.2 % | ISO 527-1/-2 | Cond., 23°C |
断裂(brk) | 2.2 % | ISO 527-1/-2 | Dry, 23°C |
弯曲强度 | |||
- | 210 Mpa | ISO 178 | Cond. |
- | 220 Mpa | ISO 178 | Dry |
弯曲模量 | 10500 Mpa | ISO 178 | Cond., 23°C |
弯曲模量 | 10500 Mpa | ISO 178 | Dry, 23°C |
拉伸模量 | 10500 Mpa | ISO 527-1/-2 | Cond., 23°C |
拉伸模量 | 7500 Mpa | ISO 527-1/-2 | Dry, 120°C |
拉伸模量 | 10500 Mpa | ISO 527-1/-2 | Dry, 23°C |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 6.5 kJ/m² | ISO 179/1eA | Cond. |
23℃ (73℉) | 6.5 kJ/m² | ISO 179/1eA | Dry |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | 60 kJ/m² | ISO 179/1eU | Dry |
23℃ (73℉) | 50 kJ/m² | ISO 179/1eU | Cond. |
23℃ (73℉) | 60 kJ/m² | ISO 179/1eU | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 265 °C | ISO 75-1/-2 | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 19 E-6/K | ISO 11359-1/-2 | (23-55)°C |
横向(Across Flow) | 53 E-6/K | ISO 11359-1/-2 | (23-55)°C |
熔融温度(Tm) | 300 °C | ISO 11357-1/-3 | DSC |
加工温度 | 310~340 °C | - | Injection moulding/Extrusion |
加工温度 | 330 °C | - | Test specimen production |
模具温度 | 100~160 °C | - | Injection moulding |
模具温度 | 140 °C | - | Test specimen production |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-0 | 0.25 mm | UL94 | |
V-0 | 0.25 mm | IEC 60695-11-10 | |
V-0 | 1.5 mm | IEC 60695-11-10 | |
灼热丝可燃性指数(GWFI) | |||
1mm | 960 °C | IEC 60695-2-12 | |
灼热丝点燃温度(GWIT) | |||
1.0mm | 775 °C | IEC 60695-2-13 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+13 Ohm-m | IEC 62631-3-1 | Cond. |
体积电阻率 | 1.0E+13 Ohm-m | IEC 62631-3-1 | Dry |
表面电阻率 | 1.0E+15 Ohm | IEC 62631-3-2 | Cond. |
相比漏电起痕指数(CTI ) | |||
溶液A | 600 V | IEC 60112 | Cond. |
绝缘强度 | 44 kV/mm | IEC 60243-1 | Cond., K20/K20, (60*60*1 mm³) |
绝缘强度 | 45 kV/mm | IEC 60243-1 | Dry, K20/K20, (60*60*1 mm³) |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。