ULTEM 1000P200 Resin is an unreinforced amorphous polyetherimide (PEI) powder. This powder is available with an average particle size (D50) of 200 micron and a maximum particle size (D100) of 450 micron.. It may offer a high glass transition temperature (Tg) of 217°C. Features are excellent mechanical, electrical and dimensional properties up to high temperatures. The material may offer very good chemical resistance for an amorphous material and is inherently flame retardant. The material is RoHS Compliant. The base material is transparent amber colored.
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐热阻燃尺寸稳定耐化学性耐水解溶于环氧树脂 | |||
| 颜色形状 | 粉末状透明褐色 | |||
| 成型方式 | 烧结浸渍法(复合)静电/粉末喷涂 | |||
| 法规认证 | RoHS(欧盟电子电气设备中有害物质) | |||
| 曲线坐标点 | N粘度-剪切速度剪切应力-剪切速率动态剪切模量-温度应力-应变正割模量-应变比容-温度(pvT) | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.27 g/cm³ | ISO 1183 | |
比重 | 1.27 g/cm³ | ASTM D792 | |
熔体体积流动速率(MVR) | |||
360°C/5.0 kg | 13 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
337°C/6.6 kg | 9 g/10 min | ASTM D 1238 | |
吸水率 | 0.25 % | ASTM D570 | 23°C/24hrs |
吸水率 | 1.25 % | ASTM D570 | 23°C/Saturated |
吸水率 | 0.25 % | ISO 62-1 | 23°C/24hrs |
吸水率 | 1.25 % | ISO 62-1 | 23°C/saturated |
吸湿率 | 0.2 % | ISO 62-4 | 23°C/50% RH/24hrs |
吸湿率 | 0.7 % | ISO 62-4 | 23°C/50% RH/Equilibrium |
磨耗 | 10 mg/1000cy | ASTM D 1044 | Taber Abrasion, CS-17, 1 kg |
粒子大小 | 200 micrometer | Internal | Mean Resin Particle Size |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 110 Mpa | ASTM D638 | Type I, 5 mm/min |
屈服(yld) | 115 Mpa | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 110 Mpa | ISO 527 | 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 7 % | ASTM D638 | Type I, 5 mm/min |
屈服(yld) | 7 % | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 6 % | ISO 527 | 50 mm/min |
断裂(brk) | 60 % | ASTM D638 | Type I, 5 mm/min |
断裂(brk) | 60 % | ASTM D638 | Type I, 50 mm/min |
断裂(brk) | 50 % | ISO 527 | 50 mm/min |
弯曲强度 | |||
屈服(yld) | 165 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
屈服(yld) | 160 Mpa | ASTM D790 | 2.6 mm/min, 100 mm span |
屈服(yld) | 160 Mpa | ISO 178 | 2 mm/min |
弯曲模量 | 3200 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 3400 Mpa | ASTM D790 | 2.6 mm/min, 100 mm span |
弯曲模量 | 3300 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 3350 Mpa | ASTM D638 | 5 mm/min |
拉伸模量 | 3200 Mpa | ISO 527 | 1 mm/min |
泊松比 | 0.36 - | ASTM E 132 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 4 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm |
23℃ (73℉) | 4 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 50 J/m | ASTM D256 | |
-30℃ (-22℉) | 6 kJ/m² | ISO 180/1A | 80*10*4 |
23℃ (73℉) | 53 J/m | ASTM D256 | |
23℃ (73℉) | 6 kJ/m² | ISO 180/1A | 80*10*4 |
悬臂梁无缺口(Izod Unnotched) | |||
-30℃ (-22℉) | NB kJ/m² | ISO 180/1U | 80*10*4 |
-30℃ (-22℉) | 1540 J/m | ASTM D 4812 | |
23℃ (73℉) | 1800 J/m | ASTM D4812 | |
23℃ (73℉) | NB kJ/m² | ISO 180/1U | 80*10*4 |
落锤冲击 | 36 J | ASTM D 3029 | Gardner, 23°C |
反向冲击 | |||
悬臂梁缺口冲击23°C | 1335 J/m | ASTM D 256 | 3.2 mm |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度 M | 106 M | ISO 2039-2 | |
洛氏硬度 M | 109 M | ASTM D 785 | |
球压硬度 | 140 Mpa | ISO 2039-1 | H358/30 |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 207 °C | ASTM D648 | 3.2 mm, unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | 210 °C | ASTM D648 | 6.4 mm, unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | 209 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | 190 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 201 °C | ASTM D648 | 6.4 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 192 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
维卡软化温度(Vicat) | 211 °C | ASTM D1525 | Rate B/50 |
维卡软化温度(Vicat) | 211 °C | ISO 306/B50 | |
维卡软化温度(Vicat) | 215 °C | ISO 306/A50 | |
维卡软化温度(Vicat) | 212 °C | ISO 306/B120 | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 56 E-6/°C | ASTM E831 | -20°C to 150°C, flow |
纵向(Flow) | 52 E-6/°C | ISO 11359-2 | -20°C to 150°C, flow |
横向(Across Flow) | 54 E-6/°C | ASTM E831 | -20°C to 150°C, xflow |
横向(Across Flow) | 52 E-6/°C | ISO 11359-2 | -20°C to 150°C, xflow |
导热系数 | 0.22 W/m-°C | ISO 8302 | |
导热系数 | 0.22 W/m-°C | ASTM C 177 | |
球压痕温度 | 125 °C | IEC 60695-10-2 | PASS |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
氧指数(LOI) | 47 % | ASTM D 2863 | |
氧指数(LOI) | 47 % | ISO 4589 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+17 Ohm-cm | ASTM D257 | |
体积电阻率 | 1.0E+15 Ohm-cm | IEC 60093 | |
表面电阻率 | 1.0E+15 Ohm | IEC 60093 | ROA |
介电常数(DK) | |||
50/60 Hz | 2.9 - | IEC 60250 | |
100Hz | 3.15 - | ASTM D 150 | |
1 kHz | 3.15 - | ASTM D 150 | |
1MHz | 2.9 - | IEC 60250 | |
1.1 GHz | 3.01 - | Internal | |
5 GHz | 3.02 - | Internal | |
10 GHz | 3.02 - | Internal | |
耗散因数(DF) | |||
50/60 Hz | 5 E-4 | IEC 60250 | |
100Hz | 15 E-4 | ASTM D 150 | |
1 kHz | 12 E-4 | ASTM D 150 | |
1MHz | 60 E-4 | IEC 60250 | |
1.1 GHz | 12 E-4 | Internal | |
5 GHz | 24 E-4 | Internal | |
10 GHz | 27 E-4 | Internal | |
相对漏电起痕指数(CTI ) | |||
- | 150 V | IEC 60112 | |
- | 100 V | IEC 60112 | M |
绝缘强度 | 32.7 kV/mm | ASTM D149 | in air, 1.6 mm |
绝缘强度 | 28 kV/mm | ASTM D149 | in oil, 1.6 mm |
绝缘强度 | 19.7 kV/mm | ASTM D149 | in oil, 3.2 mm |
绝缘强度 | 33 kV/mm | IEC 60243-1 | in oil, 0.8 mm |
绝缘强度 | 25 kV/mm | IEC 60243-1 | in oil, 1.6 mm |
绝缘强度 | 16 kV/mm | IEC 60243-1 | in oil, 3.2 mm |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。