VALOX VIC4311 is a 30% glass filled, impact modified PBT with excellent epoxy adhesion. Automotive underhood applications such as ignition coil housings.
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 增韧/冲击改性良好粘合性填充增强 | |||
| 添加助剂 | 抗冲击剂 | |||
| 增强填充 | 30% 玻纤 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.42 g/cm³ | ISO 1183 | |
比重 | 1.42 - | ASTM D792 | |
熔体体积流动速率(MVR) | |||
250°C/5.0 kg | 15 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
250°C/5.0 kg | 19 g/10 min | ASTM D1238 | |
收缩率 | |||
纵向(Flow) | 0.2~0.4 % | Internal | flow, 3.2 mm |
纵向(Flow) | 0.6~0.8 % | Internal | flow, 6.4 mm |
横向(Across Flow) | 0.6~0.8 % | Internal | xflow, 3.2 mm |
吸水率 | 0.09 % | ISO 62 | (23°C/sat) |
吸湿率 | 0.07 % | ISO 62 | 23°C / 50% RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 83 Mpa | ASTM D638 | Type I, 5 mm/min |
屈服(yld) | 86 Mpa | ISO 527 | 5 mm/min |
断裂(brk) | 84 Mpa | ISO 527 | 5 mm/min |
断裂(brk) | 84 Mpa | ASTM D638 | Type I, 5 mm/min |
拉伸延伸率 | |||
屈服(yld) | 3 % | ASTM D638 | Type I, 5 mm/min |
屈服(yld) | 3 % | ISO 527 | 5 mm/min |
断裂(brk) | 4 % | ASTM D638 | Type I, 5 mm/min |
断裂(brk) | 4 % | ISO 527 | 5 mm/min |
弯曲强度 | |||
屈服(yld) | 129 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
屈服(yld) | 139 Mpa | ISO 178 | 2 mm/min |
弯曲模量 | 6080 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 6180 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 8360 Mpa | ASTM D638 | 5 mm/min |
拉伸模量 | 7370 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 16 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 97 J/m | ASTM D256 | |
-30℃ (-22℉) | 9 kJ/m² | ISO 180/1A | 80*10*4 |
23℃ (73℉) | 137 J/m | ASTM D256 | |
23℃ (73℉) | 12 kJ/m² | ISO 180/1A | 80*10*4 |
仪器化落镖冲击能量 | |||
23℃ (73℉)总能量 | 13 J | ASTM D3763 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 220 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 205 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 175 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
维卡软化温度(Vicat) | 180 °C | ASTM D1525 | Rate B/50 |
维卡软化温度(Vicat) | 170 °C | ISO 306 | Rate B/120 |
维卡软化温度(Vicat) | 175 °C | ISO 306 | Rate B/50 |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 23 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
纵向(Flow) | 23 E-6/°C | ISO 11359-2 | -40°C to 40°C, flow |
横向(Across Flow) | 114 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
横向(Across Flow) | 114 E-6/°C | ISO 11359-2 | -40°C to 40°C, xflow |
- | 30 E-6/°C | TMA | -30°C to 30°C |
球压痕温度 | 75 °C | IEC 60695-10-2 | PASS |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
表面电阻率 | 1.0E+16 Ohm | ASTM D257 | |
介电常数(DK) | |||
50/60 Hz | 3 - | ASTM D150 |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。