Description/Primary Uses
• Carbon-filled PEEK
• Wear rings and bushings
• Back-up rings
• CMP retainer rings
• Supports
• Guides
• Wafer handling robot end effector pads
Features & Benefits
• High physical properties
• Excellent wear resistance and chemical compatibility
• Impact resistant
• High performance over wide range of operating conditions
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 良好冲击性耐热阻燃耐磨医疗级耐化学性填充增强 | |||
| 颜色形状 | 粒状黑色 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 碳纤 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.41 g/cm³ | ASTM D792 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 230.3 Mpa | ASTM D638 | |
拉伸延伸率 | |||
- | 1.9 % | ASTM D 638 | |
弯曲强度 | |||
- | 346.8 Mpa | ASTM D790 | |
弯曲模量 | 18960.6 Mpa | ASTM D790 | 0.5% Secant |
拉伸模量 | 21718.5 Mpa | ASTM D638 | 0.5% Secant |
摩擦系数 | 0.18 - | ASTM G77 | PV = 12600 psi-ft/min |
磨损因数 | 230 E-10 in3·min/ft·lb·hr | ASTM G77 | |
剪切强度 | 120 Mpa | ASTM D 732 | Axial |
剪切强度 | 95.8 Mpa | ASTM D 732 | Transverse |
抗压强度 | 262 Mpa | ASTM D 695 | Break |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度 M | 108 M | ASTM D 785 | |
邵氏硬度 D | 92 D | ASTM D 2240 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 316 °C | ASTM D648 | |
线性膨胀系数(CLTE) | |||
- | 18 E-6 cm/cm/℃ | ASTM D 696 | Above 149°C |
- | 9 E-6 cm/cm/℃ | ASTM D 696 | Below 149°C |
负载形变 | 0.06 % | ASTM D621 |