Roving Glass - PA6 Consolidated Composite Laminate
Tepex® is a group of composite semi-finished products that are fully impregnated, consolidated and plate-shaped. They are made of high-tensile continuous fibers (or long fibers in the case of Tepex® flowcore) and a thermoplastic matrix. These composite sheets can be processed into complex components in short cycle times through heating and subsequent forming.
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 填充增强 | |||
| 颜色形状 | 板材 | |||
| 增强填充 | 47% 玻纤 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.8 g/cm³ | ISO 1183 | Laminate density |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
- | 380 Mpa | ISO 527-4/5 | 23 °C, ISO 1110 |
- | 390 Mpa | ISO 527-4/5 | 23 °C, dry |
拉伸延伸率 | |||
断裂(brk) | 2.3 % | ISO 527-4/5 | 23 °C, ISO 1110 |
断裂(brk) | 2.2 % | ISO 527-4/5 | 23 °C, dry |
弯曲强度 | |||
- | 300 Mpa | ISO 14125 | 23 °C, ISO 1110 |
- | 580 Mpa | ISO 14125 | 23 °C, dry |
弯曲模量 | 16000 Mpa | ISO 14125 | 23 °C, ISO 1110 |
弯曲模量 | 20000 Mpa | ISO 14125 | 23 °C, dry |
拉伸模量 | 18000 Mpa | ISO 527-4/5 | 23 °C, ISO 1110 |
拉伸模量 | 23000 Mpa | ISO 527-4/5 | 23 °C, dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
- | 215 °C | ISO 75-1/-3 | 19 GPa |
线性膨胀系数(CLTE) | |||
- | 16 E-6/K | ISO 11359-1/-2 | -35 °C to 23 °C, dry |
- | 16 E-6/K | ISO 11359-1/-2 | 23 °C to 80 °C, dry |
熔融温度(Tm) | 220 °C | ISO 11357-3 | 10 K/min |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。